Methods of forming trench isolation in the fabrication of integrated circuitry, methods of fabricating memory circuitry, integrated circuitry and memory integrated circuitry

ABSTRACT

The invention includes methods of forming trench isolation in the fabrication of integrated circuitry, methods of fabricating integrated circuitry including memory circuitry, and integrated circuitry such as memory integrated circuitry.

TECHNICAL FIELD

This invention relates to methods of forming trench isolation in the fabrication of integrated circuitry, to methods of fabricating integrated circuitry including memory circuitry, and to integrated circuitry including memory integrated circuitry.

BACKGROUND OF THE INVENTION

In the fabrication of integrated circuitry, numerous devices are packed onto a single small area of a semiconductor substrate to create an integrated circuit. Many of the individual devices are electrically isolated from one another. Accordingly, electrical isolation is an integral part of semiconductor device design for preventing unwanted electrical coupling between adjacent components and devices.

As the size of integrated circuits is reduced, the devices that make up the circuits are positioned closer together. Conventional methods of isolating circuit components use trench isolation. Such is typically formed by etching trenches into a semiconductor substrate and filling the trenches with insulative material. As the density of components on the semiconductor substrate increased, the widths of the trenches have decreased. Further, it is not uncommon to find different areas of a substrate as having different width and/or different depth isolation trenches. Also and regardless, some areas of integrated circuitry have greater minimum active area spacing between isolation trenches than do other areas.

Insulative materials that are commonly utilized for electrical isolation within isolation trenches include silicon dioxide and silicon nitride. For example, it is common to thermally oxidize trench sidewalls within a silicon-comprising semiconductor substrate, and provide a thin silicon nitride layer thereover. The remaining volume of the trenches is then filled with an insulative material, for example high density plasma deposited silicon dioxide. Yet as trenches have become deeper and narrower, high density plasma deposited oxides can result in undesired void formation within the trenches during filling. Alternate techniques which provide better conformal deposition within isolation trenches include spin-on-glass and chemical vapor deposition utilizing ozone and tetraethylorthosilicate (TEOS). Such latter processes, while resulting in good void-free gap filling, typically result in a silicon dioxide deposition which is not as dense as desired. Accordingly, a steam anneal at very high temperatures is typically utilized to densify the deposited silicon dioxide. To preclude undesired oxide formation of underlying material, a silicon nitride oxidation barrier layer is typically employed within all of the trenches to shield underlying material from being oxidized during the steam anneal. Yet in some instances, it is undesirable to have a silicon nitride layer received next to the edges of active devices. This is particularly so in tight isolation spaced regions due to either silicon nitride's high dielectric constant or its ability to charge up by storing injected electrons which may compromise the performance of the devices.

While the invention was motivated in addressing the above identified issues, it is in no way so limited. The invention is only limited by the accompanying claims as literally worded, without interpretative or other limiting reference to the specification, and in accordance with the doctrine of equivalents.

SUMMARY

The invention includes methods of forming trench isolation in the fabrication of integrated circuitry, methods of fabricating memory circuitry, and memory integrated circuitry. In one implementation, first and second isolation trenches are formed into semiconductive material of a semiconductor substrate. The first isolation trench has a narrowest cross sectional dimension which is less than that of the second isolation trench. A first insulative material is deposited to within the first and second isolation trenches effective to fill remaining volume of the first isolation trench within the semiconductive material but not that of the second isolation trench within the semiconductive material. An intermediate insulative material lining is deposited over the first insulative material within the second isolation trench within the semiconductive material, but not within the first isolation trench within the semiconductive material. The intermediate insulative material lining comprises opposing sidewalls that face one another within the semiconductive material and a base surface extending from and between the opposing and facing sidewalls within the semiconductive material. After the depositing of the intermediate insulative material lining, a second insulative material is deposited over the opposing and facing sidewalls, and over the base surface, effective to fill remaining volume of the second isolation trench within the semiconductive material. The intermediate insulative material lining is different from that of the first and second insulative materials.

In one implementation, a method of forming integrated circuitry, comprising forming isolation trenches within semiconductive material of a first area of circuitry of a semiconductor substrate and within semiconductive material of a second area of circuitry of the semiconductor substrate. The first circuitry area comprises a first minimum active area spacing between the isolation trenches received therein and the second circuitry area comprising a second minimum active area spacing between the isolation trenches received therein. The first minimum active area spacing is less than the second minimum active area spacing. A first insulative material is deposited to within the isolation trenches of the first circuitry area and to within the isolation trenches of the second circuitry area. The first insulative material less than fills remaining volume of the isolation trenches within the semiconductive material of the second circuitry area. After depositing the first insulative material, an insulative nitride-comprising layer is deposited to within the isolation trenches within the semiconductive material of the second circuitry area but not to within the isolation trenches within the semiconductive material of the first circuitry area. The insulative nitride-comprising layer comprises opposing sidewalls that face one another within the semiconductive material and a base surface extending from and between the opposing and facing sidewalls within the semiconductive material.

In one implementation, a method of fabricating memory circuitry, comprises forming isolation trenches within semiconductive material of a memory array area of a semiconductor substrate and within semiconductive material of a peripheral circuitry area of the semiconductor substrate. A first insulative material is deposited to within the isolation trenches of the memory array area and to within the isolation trenches of the peripheral circuitry area. The first insulative material less than fills remaining volume of the isolation trenches within the semiconductive material of the peripheral circuitry area. After depositing the first insulative material, an insulative nitride-comprising layer is deposited to within the isolation trenches within the semiconductive material of the peripheral circuitry area but not to within the isolation trenches within the semiconductive material of the memory array area. The insulative nitride-comprising layer comprises opposing sidewalls that face one another within the semiconductive material and a base surface extending from and between the opposing and facing sidewalls within the semiconductive material.

In one implementation, integrated circuitry comprises a semiconductor substrate comprising a first circuitry area and a second circuitry area. The first circuitry area comprises a first minimum active area spacing between the isolation trenches received therein and the second circuitry area comprising a second minimum active area spacing between the isolation trenches received therein. The first minimum active area spacing is less than the second minimum active area spacing. Isolation trenches are received within semiconductive material of the semiconductor substrate within the first circuitry area and within the second circuitry area. Insulative material is received within the isolation trenches within the semiconductive material within the first circuitry array area and within the second circuitry area. In one aspect, all insulative material within the first circuitry array area isolation trenches is void of any insulative aluminum oxide, with insulative material received within the isolation trenches within the second circuitry area comprising an insulative aluminum oxide-comprising layer. In one aspect, all insulative material within the first circuitry array area isolation trenches is void of any insulative nitride, with insulative material received within the isolation trenches within the second circuitry area comprising an insulative nitride-comprising layer. The insulative nitride-comprising layer comprises opposing sidewalls that face one another within the semiconductive material and a base surface extending from and between the opposing and facing sidewalls within the semiconductive material.

Other implementations and aspects are contemplated.

BRIEF DESCRIPTION OF THE DRAWINGS

Preferred embodiments of the invention are described below with reference to the following accompanying drawings.

FIG. 1 is a fragmentary diagrammatic sectional view of a substrate in process in accordance with an aspect of the invention.

FIG. 2 is a view of the FIG. 1 substrate at a processing subsequent to that shown by FIG. 1.

FIG. 3 is a view of the FIG. 2 substrate at a processing subsequent to that shown by FIG. 2.

FIG. 4 is a view of the FIG. 3 substrate at a processing subsequent to that shown by FIG. 3.

FIG. 5 is a view of the FIG. 4 substrate at a processing subsequent to that shown by FIG. 4.

FIG. 6 is a view of the FIG. 5 substrate at a processing subsequent to that shown by FIG. 5.

FIG. 7 is a view of the FIG. 6 substrate at a processing subsequent to that shown by FIG. 6.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

This disclosure of the invention is submitted in furtherance of the constitutional purposes of the U.S. Patent Laws “to promote the progress of science and useful arts” (Article 1, Section 8).

The invention contemplates methods of forming trench isolation in the fabrication of integrated circuitry and, in one exemplary preferred embodiment, in the fabricating of memory circuitry. Referring initially to FIG. 1, a semiconductor substrate is indicated generally with reference numeral 10. In the context of this document, the term “semiconductor substrate” or “semiconductive substrate” is defined to mean any construction comprising semiconductive material, including, but not limited to, bulk semiconductive materials such as a semiconductive wafer (either alone or in assemblies comprising other materials thereon), and semiconductive material layers (either alone or in assemblies comprising other materials). The term “substrate” refers to any supporting structure, including, but not limited to, the semiconductive substrates described above. In one exemplary embodiment, FIG. 1 can be considered as depicting a first circuitry area 12 of semiconductor substrate 10 and a second circuitry area 14 of semiconductor substrate 10. In one exemplary implementation, the integrated circuitry being fabricated comprises memory circuitry with first circuitry area 12 comprising a memory array area and second circuitry area 14 comprising a peripheral circuitry area. In one exemplary implementation, the integrated circuitry comprises logic circuitry, with first circuitry area 12 comprising a logic circuitry area and second circuitry area 14 comprising metal routing area.

Semiconductor substrate 10 is depicted as comprising bulk semiconductive material 16, for example lightly doped monocrystalline silicon. Of course, semiconductor-on-insulator constructions and other substrates, whether existing or yet-to-be developed, are also contemplated. A pad oxide layer 18 has been formed over semiconductive material 16, and a silicon nitride masking layer 20 formed over pad oxide layer 18.

Referring to FIG. 2, first isolation trenches 22, 22 a and second isolation trenches 24, 24 a, have been formed into semiconductive material 16 of semiconductor substrate 10. By way of example only, an exemplary technique for doing so comprises photolithographic patterning and etch. Trenches 22 and 22 a might be of the same size and configuration or of different size and configuration relative to one another. Likewise, trenches 24 and 24 a might be of the same size and configuration or of different size and configuration relative to one another. In one exemplary embodiment, isolation trenches 22, 22 a as formed within semiconductive material 16 are formed within first circuitry area 12, while isolation trenches 24, 24 a are formed within semiconductive material 16 received within second circuitry area 14. More than the illustrated pairs of such trenches would typically be fabricated in each of the respective areas, with only two of such trenches in each area being shown for clarity. Also, aspects of the invention contemplate fabrication with respect to only two different dimensioned trenches. In the depicted exemplary embodiment, at least one of first isolation trenches 22, 22 a has a narrowest cross sectional dimension “A” which is less than that of at least one of second isolation trenches 24, 24 a and which is depicted by dimension “B”. By way of example only, an exemplary narrowest dimension A for isolation trenches 22, 22 a is 500 Angstroms, while that for narrowest dimension B of second isolation trenches 24, 24 a is 1000 Angstroms. Further and regardless, in one exemplary aspect of the invention, first circuitry area 12 comprises a first minimum active area spacing C between isolation trenches 22, 22 a received therein and the second circuitry area comprises a second minimum active area spacing D between isolation trenches 24, 24 a received therein. The first minimum active area spacing is less than the second minimum active area spacing. By way of example only, an exemplary first minimum active area spacing C is from 10 to 110 nanometers, while that for second minimum active area spacing D is from 200 to 800 nanometers.

Referring to FIG. 3, substrate 10 has been thermally oxidized to form silicon dioxide-comprising layers 26 which line each of trenches 22, 22 a and 24, 24 a. An exemplary thickness range for silicon dioxide layer 26 is from 50 Angstroms to 75 Angstroms. By way of example only, an exemplary technique or forming such layer includes furnace oxidation at 800° C., for example using O₂ and/or N₂ exposure, followed by H₂O exposure, followed again by O₂ and/or N₂ exposure. Such layer might be formed later in the process, or not at all. Regardless, isolation trenches 22, 22 a and 24, 24 a can be considered as having semiconductive material sidewalls 28 and some remaining volume 30, 30 a and 32, 32 a respectively, within semiconductive material 16.

Referring to FIG. 4, a first insulative material 34 is deposited to within first isolation trenches 22, 22 a and second isolation trenches 24, 24 a. In the depicted preferred embodiment, such first insulative material depositing is effective to fill remaining volumes 30, 30 a of first isolation trenches 22, 22 a within semiconductive material 16, but not those remaining volumes 32, 32 a of second isolation trenches 24, 24 a within semiconductive material 16. In one preferred embodiment, the depositing of first insulative material 34 is to no greater than 20% of the depth of the remaining volume of one of the second isolation trenches at the start of the depositing of first insulative material 34, with such “depth” referred to as being that of the trench 24 within semiconductive material 16. Further in one preferred embodiment, the depositing of first insulative material 34 is from 10% to 20% of such depth of the trenches 24 within semiconductive material 16. Further in one preferred embodiment, the depositing of first insulative material 34 is from 200 Angstroms to 600 Angstroms thick.

By way of example only, one preferred technique for depositing first insulative material 34 is by atomic layer deposition/depositing (ALD). By way of example only, an exemplary first insulative material is silicon dioxide, which can be deposited by ALD using hexachlorodisilane or dichlorosilane and O₃ or O₂ plasma as deposition precursors. ALD typically involves formation of successive atomic layers on a substrate. Described in summary, ALD includes exposing an initial substrate to a first chemical species to accomplish chemisorption of the species onto the substrate. Theoretically, the chemisorption forms a monolayer that is uniformly one atom or molecule thick on the entire exposed initial substrate. In other words, a saturated monolayer is preferably formed. Practically, chemisorption might not occur on all portions or completely over the desired substrate surfaces. Nevertheless, such an imperfect monolayer is still considered a monolayer in the context of this document. In many applications, merely a substantially saturated monolayer may be suitable. A substantially saturated monolayer is one that will still yield a deposited layer exhibiting the quality and/or properties desired for such layer.

The first species is purged from over the substrate and a second chemical species is provided to chemisorb onto the first monolayer of the first species. The second species is then purged and the steps are repeated with exposure of the second species monolayer to the first species. In some cases, the two monolayers may be of the same species. Also, a third species or more may be successively chemisorbed and purged just as described for the first and second species. Further, one or more of the first, second and third species can be mixed with inert gas to speed up pressure saturation within a reaction chamber.

Purging may involve a variety of techniques including, but not limited to, contacting the substrate and/or monolayer with a carrier gas and/or lowering pressure to below the deposition pressure to reduce the concentration of a species contacting the substrate and/or chemisorbed species. Examples of carrier gases include nitrogen, Ar, He, Ne, Kr, Xe, etc. Purging may instead include contacting the substrate and/or monolayer with any substance that allows chemisorption byproducts to desorb and reduces the concentration of a species preparatory to introducing another species. A suitable amount of purging can be determined experimentally as known to those skilled in the art. Purging time may be successively reduced to a purge time that yields an increase in film growth rate. The increase in film growth rate might be an indication of a change to a non-ALD process regime and may be used to establish a purge time limit.

ALD is often described as a self-limiting process in that a finite number of sites exist on a substrate to which the first species may form chemical bonds. The second species might only bond to the first species and thus may also be self-limiting. Once all of the finite number of sites on a substrate are bonded with a first species, the first species will often not bond to other of the first species already bonded with the substrate. However, process conditions can be varied in ALD to promote such bonding and render ALD not self-limiting. Accordingly, ALD may also encompass a species forming other than one monolayer at a time by stacking of a species, forming a layer more than one atom or molecule thick. Further, local chemical reactions can occur during ALD (for instance, an incoming reactant molecule can displace a molecule from an existing surface rather than forming a monolayer over the surface). To the extent that such chemical reactions occur, they are generally confined within the uppermost monolayer of a surface.

Traditional ALD can occur within frequently-used ranges of temperature and pressure and according to established purging criteria to achieve the desired formation of an overall ALD layer one monolayer at a time. Even so, ALD conditions can vary greatly depending on the particular precursors, layer composition, deposition equipment, and other factors according to criteria known by those skilled in the art. Maintaining the traditional conditions of temperature, pressure, and purging minimizes unwanted reactions that may impact monolayer formation and quality of the resulting overall ALD layer. Accordingly, operating outside the traditional temperature and pressure ranges may risk formation of defective monolayers.

Further by way of example only, and wherein first insulative material 34 comprises silicon dioxide, an exemplary depositing therof comprises: i) depositing a layer comprising a metal over outer surfaces within first isolation trenches 22, 22 a and second isolation trenches 24, 24 a, followed by ii) flowing a silanol to the metal of the outer surfaces effective to deposit a silicon dioxide-comprising layer within first isolation trenches 22, 22 a and second isolation trenches 24, 24 a. Preferred techniques for doing so are as described in our co-pending U.S. patent application Ser. No. 10/806,923, filed on Mar. 22, 2004, entitled “Methods of Depositing Silicon Dioxide-Comprising Layers in the Fabrication of Integrated Circuitry, Methods of Forming Trench Isolation, and Methods of Forming Arrays of Memory Cells”, naming Weimin Michael Li and Gurtej S. Sandhu as inventors, the complete application of which is herein incorporated by reference.

Preferred outer surfaces within first isolation trenches 22, 22 a and second isolation trenches 24, 24 a within semiconductive material 16 comprise at least one of silicon and silicon dioxide. The layer comprising a metal is deposited thereover, and might be comprised in elemental or alloy form, but more likely will be in a metal compound form. Regardless, exemplary preferred metals include any of aluminum, yttrium, zirconium, hafnium, and mixtures thereof, with aluminum being one preferred example. A specific preferred example is an aluminum metal compound comprising methyl aluminum and aluminum oxide, for example a chemisorbed Al—O—CH₃ species. Such can be formed by chemical vapor deposition, atomic layer deposition or any other deposition, whether existing or yet-to-be developed. An exemplary technique to produce the described chemisorbed species includes atomic layer deposition whereby the outer surface is initially hydroxylated to form pending/chemisorbed OH groups. Trimethylaluminum or aluminum dimethylamide, for example, can then be provided to produce an Al—O—CH₃ layer, for example as described in Hausmann et al., Rapid Vapor Deposition of Highly Conformal Silicon Nanolaminates, Science Magazine, Vol. 298, pp. 402-406 (2002). Such might produce the described layer, and might also produce alternately, or in combination therewith, a dimethylaluminide molecule with the aluminum atoms bonded to a single oxygen atom pending from the substrate. Other aluminum containing materials are, of course, contemplated. Regardless, in one preferred implementation, the aluminum layer which is formed would preferably be no more than four monolayers thick, and perhaps most preferably only be about a single monolayer (preferably saturated) thick. Regardless, any other possibility employing aluminum or other metal is also, of course, contemplated.

In such implementation, a silanol is flowed to the metal-comprising layer. Exemplary preferred silanols include alkoxy silanols, which by definition include any alkoxy silane alcohol, for example alkoxy silane diols and alkoxy silane triols. In one preferred implementation, the depositing of first insulative material 34 using such method is self-limiting to silicon dioxide-comprising deposition after completing such depositing of the layer comprising the metal. Preferred and other exemplary attributes are preferably as described in our co-pending U.S. patent application Ser. No. 10/806,923 described above.

Further by way of example only, another preferred technique where the first insulative material comprises silicon dioxide includes flowing TEOS to the substrate.

Referring to FIG. 5, an intermediate insulative material lining 40 is deposited over first insulative material 34, and preferably “on” (meaning in at least some direct physical contact therewith) first insulative material 34 as shown within second isolation trenches 24, 24 b within semiconductive material 16. In one preferred implementation, intermediate insulative material lining 40 is not deposited to within first isolation trenches 22, 22 a. Exemplary preferred compositions for, intermediate insulative material lining 40 include insulative nitrides (i.e., Si₃N₄ and AlN) and Al₂O₃. An exemplary preferred deposition thickness for intermediate insulative material lining 40 is from about 50 Angstroms to about 150 Angstroms. In one implementation in a method of fabricating integrated circuitry, such includes depositing an insulative nitride-comprising layer (i.e., material 40) to within isolation trenches 24, 24 a within semiconductive material 16 of second circuitry area 14, but not to within isolation trenches 22, 22 a within semiconductive material 16 of first circuitry area 12. Regardless, second isolation trenches 24, 24 a can be considered as respectively comprising some remaining volume 41, 41 a within semiconductive material 16 of substrate 10. Further in the depicted preferred embodiment, intermediate insulative material lining 40 is depicted as comprising opposing sidewalls 65 and 67 that face one another within semiconductive material 16, and a base surface 70 extending from and between the opposing and facing sidewalls 65 and 67 within semiconductive material 16.

Referring to FIG. 6, a second insulative material 44 has been deposited over (and preferably “on” as shown) opposing and facing sidewalls 65 and 67, and over base surface 70, effective to fill respective remaining volumes 41, 41 a of second isolation trenches 24, 24 a. The intermediate insulative material lining 40 is different in composition from that of first insulative material 34 and second insulative material 44. First insulative material 34 and second insulative material 44 might be the same or different in composition and/or method of deposition. Regardless, where the second insulative material comprises silicon dioxide, in one preferred implementation, the depositing of second insulative material 44 comprises at least one of (c) and (d), where (c) comprises depositing spin-on-glass, and where (d) comprises flowing O₃ and TEOS to the semiconductor substrate. By way of example only, a preferred technique involving ozone and TEOS includes a substrate temperature of 700° C. and a chamber pressure of 30 Torr. Further by way of example only, an exemplary furnace deposition technique using TEOS without ozone includes a temperature of from 575° C. to 700° C., a pressure range of from 500 mTorr to 800 mTorr. Second insulative material 44 might also comprise spin on glass.

As referred to in the “Background” section above, it might be desirable to density material 44 with a steam anneal, particularly where such comprises spin-on-glass and/or silicon dioxide deposited utilizing O₃ and TEOS. In such event, the intermediate insulative material lining 40 will preferably comprise an oxidation barrier material (i.e., any of the insulative nitrides and aluminum oxide referred to above). By way of example only, an exemplary densification process includes exposure at 700° C. in an O₂ ambient for 30 seconds, followed by an increase to 800° C. over 5 seconds, and then a further ramp to 1000° C. in steam for 40 minutes, followed by a 30 minute dry.

Referring to FIG. 7, in one exemplary preferred embodiment, substrate 10 has been planarized back effective to remove materials 18, 20, 34, 40 and 44 from outwardly of semiconductive material 16, thereby forming the illustrated trench isolation.

In one exemplary aspect of the invention, a method of forming trench isolation in the fabrication of integrated circuitry is disclosed independent of forming multiple isolation trenches having different narrowest cross sectional dimensions. The invention also contemplates a method of fabricating integrated circuitry which includes forming isolation trenches within semiconductive material of a first circuitry area of a semiconductor substrate and within semiconductive material of a second circuitry area of the semiconductor substrate, by way of example only as described above in connection with FIG. 2. A first insulative material is deposited to within the isolation trenches of the first circuitry area and to within the isolation trenches of the second circuitry area, with the first insulative material less than filling the remaining volume of the isolation trenches within the semiconductive material of the second circuitry area. By way of example only, such is depicted above in connection with FIG. 4. After depositing the first insulative material, an insulative nitride-comprising layer is deposited to within the isolation trenches within the semiconductive material of the second circuitry area, but not to within the isolation trenches within the semiconductive material of the first circuitry area. The insulative nitride-comprising layer comprises opposing sidewalls that face one another within the semiconductive material and a base surface extending from and between the opposing and facing sidewalls within the semiconductive material. In one preferred implementation, such a method comprises fabricating the integrated circuitry to comprise memory circuitry, with first circuitry area 14 to comprise a memory array area of dynamic random access memory (DRAM) cells. However of course, fabrication of other integrated circuitry and other memory circuitry is also contemplated, and whether such circuitry is existing or yet-to-be developed.

The invention also contemplates integrated circuitry independent of the method of fabrication. Such integrated circuitry comprises a semiconductor substrate comprising a first circuitry area and a second circuitry area. By way of example only, FIG. 7 depicts such a semiconductor substrate. Isolation trenches are received within semiconductive material of the semiconductor substrate within the first circuitry area and within the second circuitry area. Trenches 22, 22 a and 24, 24 a of FIG. 7 are exemplary such trenches, respectively.

Insulative material is received within the isolation trenches within the semiconductive material within the first circuitry area and within the second circuitry area. In one implementation, all insulative material within the first circuitry area isolation trenches is void of any insulative nitride, and where insulative material received within the isolation trenches within the second circuitry area comprises an insulative nitride-comprising layer. Such layer comprises opposing sidewalls that face one another within the semiconductive material and a base surface extending from and between the opposing and facing sidewalls within the semiconductive material. By way of example only, where material 40 within isolation trenches 24, 24 a comprises an insulative nitride, FIG. 7 depicts such an exemplary construction.

In one implementation, all insulative material within the first circuitry area trenches is void of any insulative aluminum oxide, and wherein insulative material received within the isolation trenches within the second circuitry area comprises an insulative aluminum oxide-comprising layer. Further in one implementation, such layer comprises opposing sidewalls that face one another within the semiconductive material and a base surface extending from and between the opposing and facing sidewalls within the semiconductive material. By way of example only, FIG. 7 depicts such a construction wherein material 40 comprises aluminum oxide. Preferred attributes are otherwise as described above in the construction of FIG. 7, and yet independent of the method of fabrication.

In one implementation where for example the integrated circuitry comprises memory circuitry and first circuitry area 12 comprises a memory array area comprising DRAM cells, such could be for example and by way of example only, as shown in the bitline-over-capacitor construction of FIGS. 19 and 22 of our co-pending U.S. patent application Ser. No. 10/806,923 referred to above, with isolation trenches 22, 22 a filled with insulative material of FIG. 7 of this application corresponding to trenches 133 in FIGS. 19 and 22 of our co-pending U.S. patent application Ser. No. 10/806,923 referred to above. Of course, buried bit line DRAM and other memory circuitry are also contemplated.

In one preferred embodiment, the construction also spaces any nitride liner away from the edge of the trench isolation by an amount of greater than 200 Angstroms and less than 600 Angstroms.

In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications within the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents. 

1-44. (canceled)
 45. A method of fabricating memory circuitry, comprising: forming isolation trenches within semiconductive material of a memory array area of a semiconductor substrate and within semiconductive material of a peripheral circuitry area of the semiconductor substrate; depositing a first insulative material to within the isolation trenches of the memory array area and to within the isolation trenches of the peripheral circuitry area, the first insulative material less than filling remaining volume of the isolation trenches within the semiconductive material of the peripheral circuitry area; and after depositing the first insulative material, depositing an insulative nitride-comprising layer to within the isolation trenches within the semiconductive material of the peripheral circuitry area but not to within the isolation trenches within the semiconductive material of the memory array area, the insulative nitride-comprising layer comprising opposing sidewalls that face one another within the semiconductive material and a base surface extending from and between the opposing and facing sidewalls within the semiconductive material.
 46. The method of claim 45 wherein the depositing of the first insulative material is effective to fill remaining volume of the isolation trenches within the memory array area.
 47. The method of claim 45 wherein the isolation trenches within the memory array area have respective narrowest cross sectional dimensions which are less than that of the isolation trenches within the peripheral circuitry area.
 48. The method of claim 47 wherein the depositing of the first insulative material is effective to fill remaining volume of the isolation trenches within the memory array area.
 49. The method of claim 45 wherein the insulative nitride comprises Si₃N₄.
 50. The method of claim 45 wherein the insulative nitride comprises AlN.
 51. The method of claim 45 wherein the depositing of the first insulative material comprises atomic layer depositing.
 52. The method of claim 45 wherein the first insulative material comprises silicon dioxide, the depositing of the first insulative material comprises: i) depositing a layer comprising a metal over outer surfaces within the isolation trenches of the memory array area and of the peripheral area; and ii) flowing a silanol to the metal of the outer surfaces effective to deposit a silicon dioxide-comprising layer within the isolation trenches of the memory array area and of the peripheral area.
 53. The method of claim 52 wherein the metal comprises a metal compound.
 54. The method of claim 52 wherein the metal comprises one of aluminum, yttrium, zirconium, hafnium and mixtures thereof.
 55. The method of claim 54 wherein the metal comprises aluminum.
 56. The method of claim 52 wherein the metal-comprising layer is no more than 4 monolayers thick.
 57. The method of claim 52 wherein the depositing of the first insulative material is self limiting to silicon dioxide-comprising deposition after completing said depositing the layer comprising the metal.
 58. The method of claim 45 comprising after the depositing of the insulative nitride-comprising layer, depositing a second insulative material effective to fill remaining volume of the second isolation trench.
 59. The method of claim 58 wherein the first and second insulative materials are the same.
 60. The method of claim 58 wherein the first and second insulative materials are different.
 61. The method of claim 58 wherein the second insulative material comprises silicon dioxide, the depositing of the second insulative material comprises at least one of (c) and (d), where (c) comprises depositing spin on glass; and where (d) comprises flowing O₃ and TEOS to the semiconductor substrate.
 62. The method of claim 61 wherein the depositing of the second insulative material comprises (c).
 63. The method of claim 61 wherein the depositing of the second insulative material comprises (d).
 64. The method of claim 45 comprising fabricating the memory array area to comprise DRAM cells. 65-86. (canceled) 